Atmospheric Durability of a Triple Resin DTM Coating: Evaluation of QUV Stability, Corrosion Resistance, Chemical Spot Testing, and Heat Aging Performance in TriFLEX™

By Advanced Polymer Coatings

Protective coatings used in industrial and rail environments must demonstrate resistance to a variety of atmospheric stressors, including UV radiation, condensation, humidity, elevated temperature, and chemical splash exposure. TriFLEX™, a direct-to-metal (DTM) coating developed by Advanced Polymer Coatings, was engineered using a proprietary triple-resin formulation to address these challenges in a single-coat system.

 

Atmospheric exposure is a significant cause of coating failure in industrial environments, particularly in assets subjected to outdoor weathering, cyclic humidity, and chemical contamination. The ability of a coating system to retain its physical and chemical properties under prolonged exposure to ultraviolet light, temperature extremes, and corrosive agents is critical to maintaining long-term asset performance and reducing lifecycle maintenance costs.
 
TriFLEX™ was developed as a next-generation DTM solution that merges the chemical durability of an epoxy with the weathering resistance of a polyurethane, enhanced by a third proprietary resin designed to fortify long-term environmental resistance. This single-coat system simplifies application while preserving the multi-functional performance required for modern asset protection. The following evaluation characterizes the atmospheric resistance of TriFLEX™ using a battery of industry-standard laboratory tests.

 

 


 

Background

Typical exterior-grade epoxy and polyurethane coatings are formulated to handle limited exposure to environmental stressors but often require multi-layer application or suffer degradation under extended service. UV degradation can cause chalking and color loss. Acid rain or splash exposure can lead to film embrittlement or failure. High humidity and thermal cycling can accelerate underfilm corrosion or lead to coating delamination.
 
TriFLEX™ addresses these limitations by integrating three resin systems into a unified film that resists breakdown through co-cured polymeric reinforcement. This paper outlines TriFLEX™'s performance under QUV accelerated weathering, dry heat aging, corrosion exposure per ISO 12944-6, and chemical spot and humidity testing.


 

Materials and Test Methods

QUV Accelerated Weathering (ASTM D4587)

 12” x 12” steel panels were sprayed with TriFLEX™ and three competitive epoxies. Each panel was partially masked to preserve an unexposed control area. Panels were subjected to 750 hours of UV exposure using UVA-340 bulbs. Color stability was measured using Lab* color space and Delta E calculations to quantify change.
 

Dry Heat Aging (120°C, 720 Hours)

Performed by GPI Laboratories Project ID: N102301.BTriFLEX. TriFLEX™ panels were exposed to 120°C for 720 hours to simulate continuous high-temperature service. The post-exposure evaluation included visual assessment per ASTM D660 and D772 and adhesion testing per ASTM D4541.
 

Corrosion Testing (ISO 12944-6:2018)

Performed by KTA-Tator, INC. Project No. 66075853-R2. Panels coated at 6.0–8.0 mils were subjected to salt spray (ISO 9227), humidity (ISO 6270-1), and cyclic aging. Each test included multiple durability classifications from C3 to C4 (Low through Very High). The assessment included rusting, blistering, cracking, and scribe creep.
 

Chemical Spot and Humidity Testing (ASTM D1308, D2247)

Panels were exposed to ten aggressive chemicals for 72 hours at 23°C. The post-exposure evaluation included blistering (ASTM D714), rusting (ASTM D610), and visual degradation. Separate humidity exposure was performed at 38°C in 100% humidity for 1000 hours.
 

Spot and Spill Acid Resistance

Panels were exposed to concentrated acids, including nitric, phosphoric, sulfuric, acetic, and hydrochloric, for up to 72 hours. Gloss loss, discoloration, and film integrity were evaluated.


 

Results and Discussion

QUV Accelerated Weathering (ASTM D4587):

After 750 hours of UVA-340 exposure, TriFLEX™ panels displayed minimal discoloration and gloss loss compared to competitive epoxy systems. Delta E measurements confirmed that TriFLEX™ maintained superior color stability, reflecting its enhanced UV resistance. The masking technique allowed for a direct comparison between exposed and unexposed sections on each panel, demonstrating the coating's ability to preserve its aesthetic properties in long-term exterior environments. This performance is attributed to including UV-stable polyaspartic and polyurethane resins within the tri-resin matrix, which effectively absorb and dissipate ultraviolet radiation without undergoing the polymer chain scission commonly observed in conventional epoxies.

Image 8-7-25 at 10.58 AM

 

Dry Heat Aging Performance (120ºC for 720 hours):

Post-exposure analysis revealed that TriFLEX™ retained structural and adhesive integrity following prolonged exposure to elevated temperatures. Panels exhibited no cracking, flaking, or blistering under ASTM D660 and D772 evaluations. Adhesion testing using ASTM D4541 showed values exceeding 3600 psi, with failure occurring cohesively within the film rather than at the substrate interface. This indicates that not only did TriFLEX™ maintain its mechanical properties under thermal load, but it may have benefited from additional cross-linking due to heat exposure.

While mild discoloration and gloss reduction were noted, these changes were superficial and did not indicate any underlying degradation of the protective film. These findings confirm that TriFLEX™ is well-suited for continuous dry heat service up to 120°C, with minimal impact on coating performance.

Image 8-7-25 at 2.47 PM

Corrosion Resistance (ISO 12944-6:2018):

Comprehensive corrosion testing conducted by KTA-Tator included neutral salt spray, humidity chamber exposure, and cyclic aging per ISO 12944-6 protocols. Across all C4 durability categories (Low, Medium, High, and Very High, Regime 1), TriFLEX™ panels met or exceeded performance requirements. Key performance indicators such as rusting (Ri 0), blistering (S0), flaking (S0), and cracking (S0) remained within the strictest allowable thresholds. Cross-cut adhesion testing consistently returned a 0 rating, confirming complete coating retention after exposure.
 
In scribe creep evaluations, corrosion propagation was minimal, averaging below the 1.5 mm requirement. Although TriFLEX™ did not meet the C4 Very High Regime 2 classification due to greater scribe creep during cyclic exposure, this failure occurred under extremely aggressive accelerated conditions that exceed standard field service severity. Overall, the results validate TriFLEX™ as a high-performance corrosion barrier, particularly in coastal or industrial atmospheres requiring extended maintenance cycles.

1-2

 

Chemical Spot and Humidity Resistance (ASTM D1308 and D2247):

TriFLEX™ demonstrated broad-spectrum chemical resistance when spot-testing with highly aggressive reagents, including concentrated acids and alkaline solutions. When exposed for 72 hours, TriFLEX™ showed minimal visual degradation, mainly limited to gloss loss or surface yellowing in the most aggressive environments. In a side-by-side comparison with a leading competitive epoxy, TriFLEX™ outperformed in aesthetic retention and film integrity. Extended humidity exposure (1000 hours, 100% humidity, at 38°C) further confirmed the robustness of the coating under prolonged moisture stress. TriFLEX™ panels displayed fewer signs of underfilm corrosion, lower blister formation, and higher overall adhesion retention than the comparator system. These findings indicate that TriFLEX™ is well-suited for applications where frequent chemical contact and high humidity may compromise traditional coatings.

Image 8-7-25 at 4-56 PM

Image 8-7-25 at 4-56 PM (1)

 

Spot and Spill Acid Resistance: 

Exposure to strong acids, including nitric, hydrochloric, phosphoric, and multiple concentrations of sulfuric acid, confirmed TriFLEX™'s ability to withstand aggressive splash and spill events without catastrophic failure. Surface observations revealed slight gloss reduction or color change, but no blistering, delamination, or substrate exposure occurred within the 72-hour test period. Only superficial effects were observed in the case of highly oxidizing acids such as nitric acid. The integrity of the film barrier remained intact, affirming TriFLEX™'s utility in sectors such as chemical transport, tank linings, and processing infrastructure, where incidental acid exposure is common.

To date, TriFLEX™ has been tested against more than 100 chemicals as part of this study, further validating its broad chemical resistance and versatility in demanding industrial environments.

Image 8-7-25 at 10.51 AM

Image 8-7-25 at 10.52 AM

 

Conclusion

TriFLEX™ demonstrates a high level of atmospheric durability that positions it as a best-in-class solution for protective DTM applications. It resists degradation from UV, high humidity, elevated temperature, and chemical exposure. The results confirm that TriFLEX™'s triple-resin design can maintain barrier performance, film integrity, and visual appearance under various atmospheric stressors. These results reinforce its role as a reliable single-coat system for long-term asset protection in harsh service environments.
 
Further testing under field-exposure scenarios is recommended to correlate laboratory findings with real-world conditions and broaden the durability profile across more application categories.

For technical inquiries or collaboration opportunities, readers are encouraged to contact the technical services team at Advanced Polymer Coatings.

x

Subscribe to Our Newsletter & Blog

Get the latest tips and news in polymer coatings delivered to your inbox and start solving tomorrow's problems today.